PatentDe  


Dokumentenidentifikation EP1023379 20.09.2001
EP-Veröffentlichungsnummer 1023379
Titel VERFAHREN ZUR HERSELLUNG THERMOPLASTISCHER ELASTOMERZUSAMMENSETZUNGEN MIT VERBESSERTEN VERARBEITUNGSEIGENSCHAFTEN
Anmelder ExxonMobil Chemical Patents Inc., Baytown, Tex., US;
Advanced Elastomer Systems, L.P., Akron, Ohio, US
Erfinder PEIFFER, G., Dennis, Annandale, US;
ELLUL, D., Maria, Silver Lake, US;
ERDERLY, C., Thomas, Baytown, US;
CHLUDZINSKI, J., James, White House Station, US;
DEKMEZIAN, Armen, Kingwood, US;
HAZELTON, R., Donald, Hudson, US;
MONTAGNA, A., Angelo, Houston, US;
ROSENBAUM, M., Barry, Shaker Heights, US
Vertreter Uexküll & Stolberg, 22607 Hamburg
DE-Aktenzeichen 69801373
Vertragsstaaten BE, DE, FR, GB, NL
Sprache des Dokument EN
EP-Anmeldetag 14.10.1998
EP-Aktenzeichen 989534888
WO-Anmeldetag 14.10.1998
PCT-Aktenzeichen US9821673
WO-Veröffentlichungsnummer 9919394
WO-Veröffentlichungsdatum 22.04.1999
EP-Offenlegungsdatum 02.08.2000
EP date of grant 16.08.2001
Veröffentlichungstag im Patentblatt 20.09.2001
IPC-Hauptklasse C08K 5/41
IPC-Nebenklasse C08K 5/42   C08L 23/02   

Beschreibung[en]

This application is a continuation-in-part of copending U.S. application S.N. 08/906,870, filed August 6, 1997, which is in turn based on provisional application 60/0022432 filed August 6, 1996.

BACKGROUND OF THE INVENTION Field of the Invention

The invention relates to a process for forming thermoplastic elastomer compositions based on a blend of a thermoplastic material and a cured elastomer.

Description of Related Art

A thermoplastic elastomer is generally defined as a polymer or blend of polymers that can be processed and recycled in the same way as a conventional thermoplastic material, yet has properties and performance similar to that of vulcanized rubber at service temperatures. Blends or alloys of plastic and elastomeric rubber have become increasingly important in the production of high performance thermoplastic elastomers, particularly for the replacement of thermoset rubber in various applications.

Polymer blends which have a combination of both thermoplastic and elastic properties are generally obtained by combining a thermoplastic polymer with an elastomeric composition in a way such that the elastomer is intimately and uniformly dispersed as a discrete particulate phase within a continuous phase of the thermoplastic. Early work with vulcanized compositions is found in U.S. Pat. No. 3,037,954 which discloses static vulcanization as well as the technique of dynamic vulcanization wherein a vulcanizable elastomer is dispersed into a resinous thermoplastic polymer and the elastomer is cured while continuously mixing and shearing the polymer blend. The resulting composition is a microgel dispersion of cured elastomer, such as butyl rubber, chlorinated butyl rubber, polybutadiene or polyisoprene in an uncured matrix of thermoplastic polymer such as polypropylene.

Depending on the ultimate application, such thermoplastic elastomer (TPE) compositions may comprise one or a mixture of thermoplastic materials such as propylene homopolymers and propylene copolymers and like thermoplastics used in combination with one or a mixture of cured or non-cured elastomers such as ethylene/propylene rubber, EPDM rubber, diolefin rubber, butyl rubber or similar elastomers. TPE compositions may also be prepared where the thermoplastic material used is an engineering resin having good high temperature properties, such as a polyamide or a polyester, used in combination with a cured or non-cured elastomer. Examples of such TPE compositions and methods of processing such compositions, including methods of dynamic vulcanization, may be found in U.S. Patents 4,130,534, 4,130,535, 4,594,390, 5,177,147 and 5,290,886, as well as in WO 92/02582.

TPE compositions are normally melt processed using conventional thermoplastic molding equipment such as by injection molding, compression molding, extrusion, blow molding or other thermoforming techniques. In such TPE compositions, the presence of the elastomeric component does not necessarily improve the processability of the composition. In fact, where the elastomeric component is partially or fully cured (cross-linked) in-situ during the mixing of the TPE polymer components (dynamically vulcanized), or where a dynamically vulcanized TPE composition is further processed, there are heavier demands placed upon processing machinery as compared with the processing of a thermoplastic composition which is free of cured elastomer. Increases such as higher motor load, head pressure and/or torque can place undesirable, unacceptable, or unattainable requirements on specific machinery. For instance, a specific extruder having a specific motor power and gearing, will reach a maximum of motor load, or head pressure, under certain melt temperature conditions for a given polymer being processed. If a polymer or polymer blend is introduced to such an extruder which has such a higher requirement for power to process at least one component, such as a polymer having higher molecular weight and/or narrower molecular weight distribution and/or lower shear sensitivity, the extruder will reach a maximum of one or several of these parameters, and be therefore limited in its ability to pump/perform at a similar level to the performance expected with a more easily processable polymer. In the alternative, if melt blending or processing machinery is to be used for certain production/extrusion, and it is not so limited, the prospect of using more power or increasing head pressure for a more difficult to extrude material would be achievable, but the user of the machinery would still nonetheless desire to conserve power.

Additionally, TPE compositions may exhibit other imperfections during extrusion, specifically film extrusion, that may be undesirable, such as melt fracture. These imperfections are undesirable from a quality standpoint. For example, melt fracture also known as "shark skin" or "orange peel", can lead to poorer optical properties and/or diminished film physical properties that are generally unacceptable. Adjustments to the extrusion process which are made to avoid the development of melt fracture generally involve a slowing down of the process which leads to a reduced rate of extrudate output.

Various prior art references generally disclose the addition of various additives to olefin polymer compositions to improve the extrusion or other properties of the polymer. For example, GB 1,104,662 teaches addition of the salt of alkyl benzene sulfonic acids to polyolefins that purportedly gives a beneficial effect on melt extrusion behavior of the polyolefin. The purported effect is the reduction of the occurrence of "shark skin" or "orange peel". Both alkali and alkaline earth metal salts of alkyl benzene sulfonic acids are said to be effective.

GB 1,078,738 discloses that addition of an "external lubricant" to high molecular weight polyolefins can, purportedly, reduce occurrence of melt fracture. Suggested as external lubricants are salts of monovalent to tetravalent metals, and saturated or unsaturated carboxylic acids containing 10 to 50 carbon atoms. Sulfonates corresponding to the fatty acid salts are also said to be suitable.

JP A 59-176339 discloses that when polyolefins are narrowed in MWD or given higher molecular weight, poor fluidity results which in turn gives rise to melt fracture. The solution suggested is addition of fluorinated compounds including potassium salts of fluoroalkylsulfonic acids. These potassium salts are said to exhibit preferable temperature dependence when compared to other cations such as sodium, calcium, lithium and ammonium. The polyolefin/salt combination is said to be effective at 230° C or higher.

DE 2,823,507 discloses calendered ethylene polymers and propylene polymers containing alkali or alkaline earth mono sulfonates such as alkyl sulfonates, alenyl sulfonates, alkylaryl sulfonates and succinic acid dialkyl ester sulfonates. Sodium or calcium mono sulfonates are preferred. A suggested benefit is purported to be outstanding separation of the polymer from calendering rolls.

Canadian Patent 731,225 discloses the use of alkali metal salts of certain monosulfonic acids as additives to crystallizable polypropylene compositions to modify the crystallization properties of the polymer. Although these compositions may also include an elastomeric polymer as an impact modifier, the reference does not indicate that the additives improve polymer processability.

There is a need therefore for a relatively inexpensive, easily implemented solution to the processing problems outlined above. Such a solution should also include a material that will readily melt or incorporate into the melted TPE and not adversely affect physical properties, not interfere with crosslinking chemistry or structure produced by that chemistry, not be extractable, or negatively impact organolleptics of shaped TPE articles. Specifically, there is a commercial need for a material that may be easily incorporated into TPE compositions, that will reduce or eliminate the increased power requirement (e.g., motor load and or torque) and increased head pressure.

SUMMARY OF THE INVENTION

The invention provides a process for forming a composition or an extruded article comprising melt blending a thermoplastic elastomer composition comprising a blend of a) a thermoplastic polymer; b) an olefinic rubber; and c) from 0.005 to 5 wt%, based on the polymeric content of said blend, of at least one sulfate or sulfonate salt having the formula (R-SOx)M where X is 3 or 4, R is an organic aliphatic radical containing from 6 to 30 carbon atoms and M is a cation selected from the group consisting of alkali metals, alkaline earth metals and ammonium; and subjecting said blended composition to crosslinking conditions to form an at least partially crosslinked composition.

The invention is based on the discovery that inclusion of the above-described sulfate or sulfonate salts in TPE molding compositions results in a marked reduction of the energy requirements for melt processing and extrusion of conventional TPE compositions. In addition, injection mold spiral flow lengths are increased and fill times are significantly lowered which leads to reduced cycle times in injection molding processes.

DETAILED DESCRIPTION OF THE INVENTION

Following is a description of the various ingredients which may be used to formulate the TPE compositions.

Thermoplastic Polymer

Thermoplastic polymers suitable for use in the present invention include amorphous, partially crystalline or essentially totally crystalline polymers selected from the group consisting of polyolefins, polyamides, polyimides, polyesters, polycarbonates, polysulfones, polylactones, polyacetals, aclylonitrile/butadiene/ styrene copolymer resins, polyphenylene oxides, ethylene-carbon monoxide copolymers, polyphenylene sulfides, polystyrene, styrene/ acrylonitrile copolymer resins, styrene/maleic anhydride copolymer resins, aromatic polyketones and mixtures thereof

Polyolefins suitable for use in the compositions of the invention include thermoplastic, at least partially crystalline polyolefin homopolymers and copolymers, including polymers prepared using Ziegler/Natta type catalysts or metallocene catalysts. They are desirably prepared from monoolefin monomers having 2 to 6 carbon atoms, such as ethylene, propylene, 1-butene, isobutylene, 1-pentene, copolymers containing these monomers, and the like, with propylene being the preferred monomer. As used in the specification and claims, the term polypropylene includes homopolymers of propylene as well as reactor copolymers of propylene which can contain 1 to 20 wt% of ethylene or an alpha-olefin comonomer of 4 to 16 carbon atoms or mixtures thereof. The polypropylene can be highly crystalline isotactic or syndiotactic polypropylene, usually having a narrow range of glass transition temperature (Tg). Commercially available polyolefins may be used in the practice of the invention.

Suitable theromplastic polyamides (nylons) comprise crystalline or resinous, high molecular weight solid polymers including copolymers and terpolymers having recurring amide units within the polymer chain. Polyamides may be prepared by polymerization of one or more epsilon lactams such as caprolactam, pyrrolidione, lauryllactam and aminoundecanoic lactam, or amino acid, or by condensation of dibasic acids and diamines. Both fiber-forming and molding grade nylons are suitable. Examples of such polyamides are polycaprolactam (nylon 6), polylauryllactam (nylon 12), polyhexamethyl-eneadipamide(nylon-6,6), polyhexamethyleneazelamide(nylon -6,9),polyhexamethylenesebacamide(nylon 6,10), polyhexa-methyleneisophthalamide(nylon-6,IP) and the condensation product of 11-amino-undecanoic acid (nylon 11). Commercially available thermoplastic polyamides may be advantageously used in the practice of this invention, with linear crystalline polyamides having a softening point or melting point between 160°C-230°C being preferred.

Suitable thermoplastic polyesters which may be employed include the polymer reaction products of one or a mixture of alphatic or aromatic polycarboxylic acids esters of anhydrides and one or a mixture of diols. Examples of satisfactory polyesters include poly (trans-1,4-cyclohexylene C2-6 alkane discarboxylates such as poly(trans-1,4-cyclohexylene succinate) and poly (trans-1,4-cyclohexylene adipate); poly (cis or trans- 1,4-cyclohexanedimethylene) alkanedicarboxylates such as poly(cis 1,4-cyclohexane-di-methylene) oxlate and poly-(cis 1,4-cyclohexane-di- methylene) succinate, poly (C2-4 alkylene terephthalates) such as polyethyl-eneterephthalate and polytetrametyleneterephthalate, poly (C2-4 alkylene isophthalates such as polyethyleneisophthalate and polytetramethylene-isophthalate Preferred polyester are derived from aromatic dicarboxylic acids such as naphthalenic or phthalic acids and C2 to C4 diols, such as polyethylene terephthalate and polybutylene terephthalate. Preferred polyesters will have a melting point in the range of 160°C to 260°C.

Poly(phenylene ether) (PPE) thermoplastic engineering resins which may be used in accordance with this invention are well known, commercially available materials produced by the oxidative coupling polymerization of alkyl substituted phenols. They are generally linear polymers having a glass transition temperature in the range of 190°C to 235°C. Examples of preferred PPE polymers include poly(2,6-dialkyl-1,4 phenylene ethers) such as poly(2,6 dimethyl-1,4-phenylenether), poly 2-methyl-6-ethyl-1, 4 phenylene ether), poly-(2,6-dipropyl-1,4-phenylene ether) and poly (2-ethyl-6-propyl-1,4-phenylene ether). These polymers, their method of preparation and blends with polystyrene are further described in U.S. Patent 3,383,435.

Other thermoplastic resins which may be used include the polycarbonate analogs of the polyesters described above such as segmented poly(ether cophthalates); polycaprolactone polymers; styrene resins such as copolymers of styrene with less than 50 mole% of acrylonitrile (SAN) and resinous copolymers of styrene, acrylonitrile and butadiene (ABS); sulfone polymers such as polyphenyl sulfone.

Olefinic Rubber

Suitable rubbery materials which may be used include monoolefin copolymeric rubbers, isobutylene copolymers and diolefin rubbers, as well as mixtures thereof.

Suitable monoolefin copolymer rubbers comprise non-polar, essentially non-crystalline, rubbery copolymers of two or more alpha-monoolefins, preferably copolymerized with at least one polyene, usually a diene. Saturated monoolefin copolymer rubber, for example ethylene-propylene copolymer rubber (EPM) can be used. However, unsaturated monoolefin rubber such as EPDM rubber is more suitable. EPDM is a terpolymer of ethylene, propylene and a non-conjugated diene. Satisfactory non-conjugated dienes include 5-ethylidene-2-norbomene (ENB); vinylnorbornene (VNB) 1,4-hexadiene; 5-methylene-2-norbornene (MNB); 1,6-octadiene, 5-methyl-1,4-hexadiene; 3,7-dimethyl-1,6-octadiene; 1,3-cyclopentadiene; 1,4-cyclohexadiene; dicyclopentadiene (DCPD).

Butyl rubbers are also useful in the compositions of the invention. As used in the specification and claims, the term "butyl rubber" includes copolymers of an isoolefin and a conjugated monoolefin, terpolymers of an isoolefin, a conjugated monoolefin and divinyl aromatic monomers, and the halogenated derivatives of such copolymers and terpolymers. The useful butyl rubber copolymers comprise a major portion of isoolefin and a minor amount, usually less than 30 wt%, of a conjugated multiolefin, and are preferably halogenated, e.g., brominated, to faciliate curing. The preferred copolymers comprise 85-99.5 wt% of a C4-7 isoolefin such as isobutylene and 15-0.5 wt% of a multiolefin of 4-14 carbon atoms, such as isoprene, butadiene, dimethyl butadiene and piperylene. Commercial butyl rubber, useful in the invention, is a copolymer of isobutylene and minor amounts of isoprene. Other butyl co- and terpolymer rubbers are illustrated by the description in U.S. Patent No. 4,916,180.

Another suitable copolymer within the scope of the olefinic rubber of the present invention is a copolymer of a C4-7 isomonoolefin and a para-alkylstyrene, and preferably a halogenated derivative thereof The amount of halogen in the copolymer, predominantly present as benzylic halogen, is from 0.1 to 10 wt%. A preferred example is the brominated copolymer of isobutylene and paramethylstyrene. These copolymers are more fully described in U.S. Patent No. 5,162,445.

Another olefinic rubber class which may be used are diolefins such as polybutadiene as well as elastomeric random copolymers of butadiene with less than 50 wt% of styrene or acrylonitrile. Other suitable diolefin materials include natural rubber or synthetic polyisoprene. Mixtures comprising two or more of the olefinic rubbers may also be used.

Depending upon the desired applications, the amount of olefinic rubber present in the composition may range from 10 to 90 wt% of the total polymer content of the composition. In most applications and particularly where the rubber component is dynamically vulcanized, the rubber component will constitute less than 70 wt%, more preferably less than 50 wt%, and most preferably 10-40 wt% of the total polymer content of the composition.

Surfactants

The surfactants useful in the present invention include one or a mixture of sulfate and sulfonate salts having the generic formula (RSOx)M wherein X is 3 or 4, R is an organic radical containing from 6 to 30 carbon atoms and M is a cation selected from the group consisting of alkali metals, alkaline earth metals and ammonium. Materials of this type are well known in the detergent art and are commercially available.

Preferred surfactants are those where R is a branched or straight chain aliphatic group including alkyl, mono or di unsaturated alkenyl, alkoxy, hydroxy substituted alkyl or alkoxy alkyL M is preferably selected from lithium, sodium, potassium, calcium or magnesium, with sodium most preferred. M may also be an ammonium cation or a quaternary ammonium cation. Suitable surfactants include sodium lauryl sulfate or sulfonate, sodium alpha olefin sulfonate, ammonium lauryl sulfate, ammonium lauryl sulfonate, sodium myristyl sulfate or sulfonate, sodium octyl sulfate, and like materials. Preferred surfactants are those where R contains 8 to 20 carbon atoms, more preferably 12 to 18 carbon atoms and where R is free of halogen, e.g., fluorine substituent groups and does not contain aromatic groups.

The selection of particular surfactant is dictated by the fact that the melting point of the surfactant should be lower than the temperature at which the polymer compositions is processed, and preferably be lower than the softening or melting point of the thermoplastic polymer component (and the rubber component) present in the blend, preferably at least 10°C lower. Since the surfactant appears to function as an external lubricant during processing, it is important that it be in the melt state along with the molten polymers being processed. Thus preferred surfacants are those with a melting point below 240°C, more preferably below 230°C and most preferably below 210°C, e.g., sodium lauryl sulfate or sulfonate or sodium alpha olefin sulfonates. On the other hand where the thermoplastic polymer being processed is of relatively high melting point, e.g., polyamides, then higher melting point surfactants may be used, e.g., the alkaline earth metal sulfate or sulfonate salts.

Another factor dictating the choice of surfactant is that it should be insoluble or only sparingly soluble in liquid or semi-liquid additive materials included in the composition, such as processing oils. Severe dilution of the surfactant by such additives will result in a diminution or loss of the enhanced melt processing characteristics of the surfactant.

The surfactant may be incorporated into the composition at a level of from 0.005 to 5 wt%, more preferably from 0.01 to 0.5 wt% and most preferably from 0.03 to 0.35 wt%, based on the polymeric content of the blend.

Additives

The compositions of the invention may include plasticizers, curatives and may also include reinforcing and non-reinforcing fillers, antioxidants, stabilizers, rubber processing oil, plasticizers, extender oils, lubricants, antiblocking agents, anti-static agents, waxes, foaming agents, pigments, flame retardants and other processing aids known in the rubber compounding art. Such additives can comprise up to 50 wt% of the total composition. Fillers and extenders which can be utilized include conventional inorganics such as calcium carbonate, clays, silica, talc, titanium dioxide, carbon black and the like. The rubber processing oils generally are paraffinic, naphthenic or aromatic oils derived from petroleum fractions, but are preferably paraffinic. The type will be that ordinarily used in conjunction with the specific rubber or rubbers present in the composition, and the quantity based on the total rubber content may range from zero up to 1-200 parts by weight per hundred rubber (phr). Plasticizers such as trimellitate esters may also be present in the composition.

Processing

The olefin rubber component of the thermoplastic elastomer is generally present as small, i.e., micro-size, particles within a continuous plastic matrix, although a co-continuous morphology or a phase inversion is also possible depending on the amount of rubber relative to plastic, and the cure system or degree of cure of the rubber. The rubber is at least partially crosslinked, and preferably is completely or fully cross-linked. The partial or complete crosslinking can be achieved by adding an appropriate rubber curative to the blend of thermoplastic polymer and rubber and vulcanizing the rubber to the desired degree under conventional vulcanizing conditions. However, it is preferred that the rubber be crosslinked by the process of dynamic vulcanization. As used in the specification and claims, the term "dynamic vulcanization" means a vulcanization or curing process for a rubber contained in a thermoplastic elastomer composition, wherein the rubber is vulcanized under conditions of high shear at a temperature above the melting point of the component thermoplastic. The rubber is thus simultaneously crosslinked and dispersed as fine particles within the matrix thermoplastic, although as noted above other morphologies may also exist. Dynamic vulcanization is effected by mixing the thermoplastic elastomer components at elevated temperature in conventional mixing equipment such as roll mills, Banbury mixers, Brabender mixers, continuous mixers, mixing extruders and the like. The unique characteristic of dynamically cured compositions is that, notwithstanding the fact that the rubber component is partially or fully cured, the compositions can be processed and reprocessed by conventional plastic processing techniques such as extrusion, injection molding, blow molding and compression molding. Scrap or flashing can be salvaged and reprocessed.

Those ordinarily skilled in the art will appreciate the appropriate quantities, types of cure systems and vulcanization conditions required to carry out the vulcanization of the rubber. The rubber can be vulcanized using varying amounts of curative, varying temperatures and varying time of cure in order to obtain the optimum crosslinking desired. Any known cure system for the rubber can be used, so long as it is suitable under the vulcanization conditions with the specific olefinic rubber or combination of rubbers being used and with the thermoplastic component. These curatives include sulfur, sulfur donors, metal oxides, resin systems, peroxide-based systems, hydrosylylation curatives, containing platinum or peroxide catalysts, both with and without accelerators and co-agents. Such cure systems are well known in the art and literature of vulcanization of elastomers.

The terms "fully vulcanized" and "completely vulcanized" as used in the specification and claims mean that the rubber component to be vulcanized has been cured to a state in which the elastomeric properties of the crosslinked rubber are similar to those of the rubber in its conventional vulcanized state, apart from the thermoplastic elastomer composition. The degree of cure can be described in terms of gel content or, conversely, extractable components. Alternatively the degree of cure may be expressed in terms of crosslink density. All of these descriptions are well known in the art, for example in U.S. Patent Nos. 5,100,947 and 5,157,081.

The processing surfactants may be included in the composition during the manufacture of the TPE composition by processes as described above, or may be later combined with pelletized TPE compositions used by a processor to manufacture shaped articles. For example, TPE extruded pellets may be thoroughly mixed with the surfactant in finely divided powder or liquid form to thoroughly coat each pellet, and the coated pellets introduced into an extruder along with any other additives used by the processor to produce extruded shaped articles by such process as injection molding, compression molding, blow molding and similar extrusion processes.

Melt processing temperatures will generally range from above the melting point of the highest melting polymer present in the TPE composition up to 300°C. Preferred processing temperatures will range from 140°C up to 250°C, more preferably from 150°C up to 225°C.

The following examples are illustrative of the invention.

TPE compositions used in the following examples are as follows:

TPE-U
A thermoplastic elastomer comprising a mixture of 100 parts by weight of EPDM rubber (VISTALON® 7500 supplied by Exxon Chemical Co.) and 50 parts by weight of isotactic polypropylene.
TPE-DO
A dynamically vulcanized version of TPE-U cured using a phenolic resin curing system and containing 107 parts by weight of paraffin oil per 100 parts by weight of EPDM.
TPE-DN
A dynamically vulcanized thermoplastic elastomer cured using a phenolic resin curing system and based on a mixture of 100 parts by weight of an elastomeric copolymer of butadiene and acrylonitrile, 35 parts by weight of isotactic polypropylene, and 50 parts by weight of a trimellitate ester plasticizer.
TPE-DS
A dynamically vulcanized blend of 100 parts by weight EPDM rubber, 41 parts by weight of isotactic polypropylene and 130 parts by weight of paraffin oil cured using a phenolic resin curing system.
TPE-DSA
Same as TPE-DS but containing 220 parts by weight isotatic polypropylene and 100 parts by weight EPDM rubber.
TPE-DSB
A dynamically vulcanized blend of 100 parts by weight EPDM rubber, 50 parts by weight isotactic polypropylene, 176 parts by weight processing oil and cured using a hydrosylylation cure system.
TPE-DXL
A dynamically vulcanized blend of EPDM rubber and polyolefin, containing low amounts of hydrocarbon oil and cured with a peroxide cure system.
TPE-DT
A dynamically vulcanized blend of butyl rubber, isotactic polypropylene, oil and curatives.

EXAMPLE 1

This example demonstrates a reduction in torque (as measured by changes in amperage) of compositions of this invention when melt processed. A pelletized form of the TPE compositions listed in Table 1 were each introduced into a Brabender™ Plasti-Corder melt mixer which was heated at 200°C. Typically, 50-60 g. of material is introduced at a rotation speed of 40 RPM. Upon complete melting, the torque remains essentially invariant with time and is used as the base value. Subsequently, measured amounts of sodium alpha-olefin sulfonate surfactant (Bio Terge® AS-90 marketed by Stepan Co., Northfield, Ill.) were added to each sample in the amounts listed in Table 1. After several minutes of mixing, the torque was again measured at 40 RPM and compared with the base value for each sample. As shown in Table 1, torque reductions ranging from 7.9 to 16.0% were achieved. Sample Surfactant CONC, (ppm) Torque Reduction (%) TPE-U 3500 7.9 TPE-U 5000 16.0 TPE-DO 3500 9.3 TPE-DO 5000 12.0 TPE-DN 3500 11.3 TPE-DN 5000 16.0

EXAMPLE 2

This example illustrates the effect of surfactants of this invention on extrusion properties. TPE-DS thermoplastic elastomer identified above in pellet form was tumbled in a drum with 1.14 g. HT100 mineral oil per pound of TPE-DS. The surfactant in powder form was then added at the levels shown in Table 2 and the material was tumbled another S hour to uniformly coat the pellets. Comparative samples of TPE-DS coated with a known processing aid (Dow Corning MB50-001 silicone rubber concentrate) were also prepared. The material identified in Table 2 as "AOK" is also a sodium salt of an alpha-olefin sulfonate available from Witco Chemical Co., Greenwich, CT. Prior to extrusion, the coated materials were run into a Berstorff ZE-43 extruder at 350 rpm and at 234°C to homogenize the dispersion. The torque for each sample processed in the extruder was measured in Amps and results are shown in Table 2. Torque % Reduction Torque Control TPE-DS 33 0.0 0.35% AS-90 31 6.1 0.5% AS-90 29 12.1 0.35% AOK 33 0.0 0.5% AOK 28 15.2 5% AOK 26 21.2 0.5% MB50-001 33 0.0 5% MB50-001 31 6.1

Samples as shown in Table 2 were then fed into a Killion 3 horsepower extruder heated to a 3 zone temperature ranging from 190°C to 200°C and extruded into ribbon through a 0.020 inch* * 1 inch = 2,54 cm slit die at a melt temperature of 215°C. Extruder parameters for each sample processed are shown in Table 3. Extruder Parameters Head Pressure psi° Amps ΔLb/hr* % Reduction Amps % Change lb/hr Control TPE-DS 450 2.7 5.16 0.0 0.0 0.35% AS-90 440 2.4 5.24 2.2 1.6 0.5% AS-90 430 2.4 5.24 4.4 1.6 0.35% AOK 430 2.4 4.92 4.4 -4.7 Slippage Minor 0.5% AOK 420 2.1 4.88 6.7 -5.4 Slippage Minor 5% AOK** 250 1.5 5.20 44.4** 0.8 0.5% MB50-001 450 2.4 5.16 0.0 0.0 5% MB50-001 380 2.1 4.6 15.6 -10.9 Slippage
°1 lb/hr = 0,453 Kg/h Δ1 psi : 1995 Pa * Output measured after 3 min run. Between runs the material was extruded for 15 mins before any readings or output measurements were taken. Between materials a purge was made.

**Duplicated 3 times.

The parameters as measured in Table 3 demonstrate a general reduction in extruder head pressure and torque as measured by the Amps. Output rate as measured in lb/hour was also not compromised and in most cases increased as compared with the control containing no processing aid. In contrast, the comparative samples containing 5% silicone polymer showed significant slippage and therefore a loss of output.

EXAMPLE 3

The same materials as described in Example 2 were injection molded using a Cincinnati Millacron 250 ton injection molder operating under the following conditions: Machine Heat Settings - Rear 182°C, Center 188°C,

Front 194°C, Nozzle 200°C.
Melt temperature - 210°C Shot Size - 0.85 inch Cushion - 0.19 inch Screw - 100 rpm Ram Velocity - 3.0 inch/sec.

Injection molding results using an 1S0 standard mold to make plaques of 2 mm thickness are shown in Table 4. Fill time (sec) Pack (sec) Hold (sec) Cooling (sec) Press. 1st Stage psi Press Back Psi Press. Hold Psi Press. Back Psi CONTROL TPE-DS 1.42 3.0 2.0 30.0 609 350 200 0 0.35% AS-90 2.167 3.0 2.0 30.0 605 350 200 0 0.5% AS-90 0.63 3.0 2.0 25.0 578 350 200 0 0.35% AOK 0.55 3.0 2.0 25 602 350 200 0 0.5% AOK 0.6 3.0 2.0 30.0 605 350 200 0 5% AOK 0.49 3.0 2.0 25.0 580 350 200 0 0.5% MB50001 0.94 3.0 2.0 30.0 589 350 200 0 5% MB50001 - 3.0 2.0 25 602 350 200 0

As shown in Table 4, the general effect of the use of the surfactants of this invention is to lower the fill time up to a factor of three, which thereby represents a potential of lowering the overall cycle time. It was also observed that at all pressures there was a significant improvement in spiral flow for additives used at the 5% by weight level. Also, mold sticking was observed in all samples containing the silicone polymer, but no mold sticking took place in samples containing the surfactants of this invention.

EXAMPLE 4

Compositions as identified in Table 5 were coated with the identified additive in the levels indicated and processed through a Berstorff extruder as described in Example 2. Viscosity measurements and torque reductions for each processed TPE sample were compared with TPE controls containing no added processing aid. ACR viscosity is shear viscosity measured using a Monsanto automatic capillary rheometer; extensional viscosity is measured using a Goettfert Rheotens rheometer. Extruder Parameters Torque Amps % Reduc. Torque Melt Press. Ext. Visc. at 190°C kPa s % Reduc. Ext. Visc. ACR Visc. at 204°C Poise % Reduc. ACR Visc. SAMPLE Control TPE-DS 42 0.0 1256 51.4 0.0 183 0.0 +0.5% AOK 42 0.0 1254 47.3 8.0 148 19.1 +1%AOK 38 9.5 1165 50.5 1.8 151 17.5 +2% AOK 38 9.5 1140 45.6 11.3 140 23.5 Control TPE-DT 47 0.0 1733 91.9 0.0 927 0.0 +0.5% AOK 45 4.3 1615 95.2 3.6 829 10.6 +1%AOK 43 8.5 1580 83.5 9.1 876 5.5 +2% AOK 40 4.8 1431 78.2 14.9 746 19.5 Control TPE-DSB 34 0.0 1292 70.3 0.0 173 0.0 +1%AOK 32 5.9 1187 89.5 27.3 111 35.8 Control TPE-DXL 62 0.0 2284 639 0.0 12144 0.0 +1% AOK 54 12.9 1991 248 61.2 1550 87.2 Control TPE-DSA 46 0.0 2134 586 0.0 671 0.0 +0.5% AOK 43 6.5 2096 620 5.8 526 21.6 +1% AOK 40 13.0 1906 444 24.2 444 33.8 +2% AOK 33 21.4 1709 402 31.4 372 44.6

Results in Table 5 show a general reduction in torque for samples containing additive vs control samples free of additive and also a general reduction in extruder melt pressure, indicating improved flow. Reductions in extensional viscosity and ACR viscosities are also demonstrated as compared with the controls.


Anspruch[de]
  1. Verfahren zur Bildung einer Zusammensetzung, bei dem eine thermoplastische Elastomerzusammensetzung schmelzgemischt wird, die
    • a. thermoplastisches Polymer,
    • b. olefinischen Kautschuk und
    • c. 0,005 bis 5 Gew.%, bezogen auf den Polymergehalt der Zusammensetzung, von mindestens einem Sulfat- oder Sulfonatsalz mit der Formel (RSOx)M umfasst, wobei X 3 oder 4 ist, R ein organischer aliphatischer Rest ist, der 6 bis 30 Kohlenstoffatome enthält, und M ein Kation ausgewählt aus der Gruppe bestehend aus Alkalimetallen, Erdalkalimetallen und Ammonium ist, und
    die gemischte Zusammensetzung Vernetzungsbedingungen ausgesetzt wird, um eine mindestens teilweise vernetzte Zusammensetzung zu bilden.
  2. Verfahren nach Anspruch 1, bei dem das Salz einen Schmelzpunkt unter dem Erweichungspunkt des thermoplastischen Polymers hat.
  3. Verfahren nach Anspruch 1, bei dem der olefinische Kautschuk in der Zusammensetzung in einem Gehalt von 10 bis 90 Gew.%, bezogen auf den gesamten Polymergehalt der Zusammensetzung, vorhanden ist, und das thermoplastische Polymer kristallines Polypropylen oder ein Copolymer von Propylen mit 1 bis 20 Gew.% Ethylen oder einem α-Olefincomonomer mit 4 bis 16 Kohlenstoffatomen oder Mischungen derselben ist.
  4. Verfahren nach einem der Ansprüche 1, 2 oder 3, bei dem das Salz ein Alkalimetallsalz eines Alkyl- oder Alkenylsulfonats ist, das 12 bis 18 Kohlenstoffatome enthält.
  5. Verfahren nach Anspruch 4, bei dem das Salz Natrium-α-olefinsulfonat ist und der Olefinkautschuk ausgewählt ist aus der Gruppe bestehend aus Ethylen/Propylen-Copolymeren, Ethylen/Propylen/nicht-konjugiertes Dien-Terpolymeren, Isobutylencopolymeren, Diolefinpolymeren und -copolymeren und Mischungen derselben.
  6. Verfahren nach Anspruch 1, bei dem der olefinische Kautschuk vollständig vernetzt ist.
  7. Verfahren nach Anspruch 1, bei dem während der Schmelzextrusion Härtungsmittel für den olefinischen Kautschuk zu der Zusammensetzung gegeben werden, um eine dynamisch vulkanisierte Zusammensetzung zu bilden, und bei dem das Schmelzmischen die Extrusion der Zusammensetzung einschließt.
Anspruch[en]
  1. A process for forming a composition comprising melt blending a thermoplastic elastomer composition comprising:
    • a. a thermoplastic polymer;
    • b. an olefinic rubber; and
    • c. from 0.005 to 5 wt%, based on the polymeric content of said composition, of at least one sulfate or sulfonate salt having the formula (RSOx) M wherein X is 3 or 4, R is an organic aliphatic radical containing from 6 to 30 carbon atoms and M is a cation selected from the group consisting of alkali metals, alkaline earth metals and ammonium;

         and subjecting said blended composition to crosslinking conditions to form an at least partially crosslinked composition.
  2. The process of claim 1 wherein said salt has a melting point lower than the softening point of said thermoplastic polymer.
  3. The process of claim 1 wherein said olefinic rubber is present in said composition at a level of 10 to 90 wt% based on the total polymer content of said composition; and wherein said thermoplastic polymer is crystalline polypropylene or a copolymer of propylene with 1-20 wt% of ethylene or an alpha-olefin comonomer of 4-16 carbon atoms or mixtures thereof.
  4. The process of any claims 1, 2, or 3 wherein said salt is an alkali metal salt of an alkyl or alkenyl sulfonate containing 12 to 18 carbon atoms.
  5. The process of claim 4 wherein said salt is a sodium alpha-olefin sulfonate and wherein said olefin rubber is selected from the group consisting of ethylene/propylene copolymers, ethylene/propylene/nonconjugated diene terpolymers, isobutylene copolymers, diolefin polymers and copolymers and mixtures thereof.
  6. The process of claim 1 wherein said olefinic rubber is completely crosslinked.
  7. The process of claim 1 wherein curatives for said olefinic rubber are added to said composition during said melt extrusion to form a dynamically vulcanized composition; and wherein said melt blending includes extrusion of said composition.
Anspruch[fr]
  1. Procédé pour la formation d'une composition, comprenant les étapes consistant à mélanger en masse fondue une composition élastomère thermoplastique comprenant :
    • a. un polymère thermoplastique ;
    • b. un caoutchouc oléfinique ; et
    • c. 0,005 à 5 % en poids, sur la base de la teneur en polymère de ladite composition, d'au moins un sel consistant en un sulfate ou sulfonate répondant à la formule (RSO)xM dans laquelle x est égal à 3 ou 4, R représente un radical aliphatique organique contenant 6 à 30 atomes de carbone et M représente un cation choisi dans le groupe consistant en des métaux alcalins, des métaux alcalino-terreux et le cation ammonium ;

         et à soumettre ladite composition mixte à des conditions de réticulation pour former une composition réticulée au moins partiellement.
  2. Procédé suivant la revendication 1, dans lequel le sel a un point de fusion inférieur au point de ramollissement du polymère thermoplastique.
  3. Procédé suivant la revendication 1, dans lequel le caoutchouc oléfinique est présent dans la composition en une teneur de 10 à 90 % en poids sur la base de la teneur totale en polymère de ladite composition ; et dans lequel le polymère thermoplastique consiste en un polypropylène cristallin ou un copolymère de propylène avec 1 à 20 % en poids d'éthylène ou d'un comonomère alpha-oléfinique ayant 4 à 16 atomes de carbone, ou leurs mélanges.
  4. Procédé suivant l'une quelconque des revendications 1, 2 et 3, dans lequel le sel est un sel de métal alcalin d'un alkyl- ou alcényl-sulfonate contenant 12 à 18 atomes de carbone.
  5. Procédé suivant la revendication 4, dans lequel le sel consiste en un alpha-oléfine-sulfonate de sodium et dans lequel le caoutchouc oléfinique est choisi dans le groupe consistant en des copolymères éthylène/propylène, des terpolymères éthylène/propylène/diène non conjugué, des copolymères d'isobutylène, des polymères et copolymères dioléfiniques et leurs mélanges.
  6. Procédé suivant la revendication 1, dans lequel le caoutchouc oléfinique est totalement réticulé.
  7. Procédé suivant la revendication 1, dans lequel des durcisseurs pour le caoutchouc oléfinique sont ajoutés à la composition au cours de l'extrusion en masse fondue afin de former une composition ayant subi une vulcanisation dynamique ; et dans lequel le mélange en masse fondue comprend une extrusion de ladite composition.






IPC
A Täglicher Lebensbedarf
B Arbeitsverfahren; Transportieren
C Chemie; Hüttenwesen
D Textilien; Papier
E Bauwesen; Erdbohren; Bergbau
F Maschinenbau; Beleuchtung; Heizung; Waffen; Sprengen
G Physik
H Elektrotechnik

Anmelder
Datum

Patentrecherche

Patent Zeichnungen (PDF)