PatentDe  


Dokumentenidentifikation EP1358452 04.10.2007
EP-Veröffentlichungsnummer 0001358452
Titel THERMOCHROMISCHE POLYMERE ZUR SCHNELLEN VISUELLEN BEWERTUNG DER TEMPERATUR
Anmelder The Board of Governors for Higher Education State of Rhode Island and Providence Plantations, Providence, R.I., US
Erfinder LUCHT, Brett L., Wakefield, RI 02879, US;
EULER, William B., Narragansett, RI 02882, US;
GREGORY, Otto J., Wakefield, RI 02879, US
Vertreter derzeit kein Vertreter bestellt
DE-Aktenzeichen 60221967
Vertragsstaaten AT, BE, CH, CY, DE, DK, ES, FI, FR, GB, GR, IE, IT, LI, LU, MC, NL, PT, SE, TR
Sprache des Dokument EN
EP-Anmeldetag 10.01.2002
EP-Aktenzeichen 027808906
WO-Anmeldetag 10.01.2002
PCT-Aktenzeichen PCT/US02/22079
WO-Veröffentlichungsnummer 2003001168
WO-Veröffentlichungsdatum 03.01.2003
EP-Offenlegungsdatum 05.11.2003
EP date of grant 22.08.2007
Veröffentlichungstag im Patentblatt 04.10.2007
IPC-Hauptklasse G01K 11/16(2006.01)A, F, I, 20051017, B, H, EP
IPC-Nebenklasse C08G 61/12(2006.01)A, L, I, 20051017, B, H, EP   

Beschreibung[en]

The invention relates to polythiophene-based temperature indicators.

Polythiophenes are known for their electrically conductive properties. One technique used to study polythiophenes is to analyse associated color changes when the temperature of the polythiophene is varied. Color changes provide insight into the electro-conductive properties of the polymer. There are numerous patent and literature citations which describe this work.

In many instances it is clearly desirable to know when an object or article reaches or has exceeded a specific temperature simply by viewing the object and noting that at least a portion of the object has exhibited a color change. Viewing includes visual observation by an individual or detection of color change by a sensor, which sensor would output a signal to be detected in any suitable manner.

As an example, in the food service industry there are hot trays and cold trays in which food is stored and/or served. If a cold tray, such as by regulation, is required to be maintained at a temperature of 3°C (38°F) or lower then a sensor system might be in place to signal (alarm) that the temperature is above 3°C (38°F). Alternatively, a thermometer might be used. However, in the food service industry, margins are thin, and unless required by regulation, sensing systems will not be used. There are innumerable situations where it would be desirable to provide a visual color indicator which would appear on an article such as a hot drink cup or stove top if the temperature were unsafe, on hot plates, freezers, etc which were, not functioning properly, or to know when desired temperatures were reached, e.g. in ovens.

ES-A-2158764, published on 01 September 2001 , discloses a thermochromic varnish comprising 1 - 99 vol. % of transparent varnish and 99 - 1 vol. % of a solution of a poly (3 - alkyl thiophene) of which the alkyl group may contain 4 to 30 carbon atoms. The varnish is a synthetic resin such as a phenolic resin, mixed with a solvent, pure or mixed with another additive such as a colophonium. Temperature changes are typically exhibited at 170 or 180 °C.

The present invention utilizes the color change characteristics of polythiophenes in a sensing system, which system will change color at a specific design temperature in a range from -40 to 180°C.

The polythiophene is generally of the structure :

  • wherein R1-R6 = a hydrogen, substituted or unsubstituted alkyl radical, substituted or unsubstituted alkoxy radical, substituted or unsubstituted aryl radical, substituted or unsubstituted thioalkyl radical substituted or unsubstituted trialkylsilyl radical, substituted or unsubstituted acyl radical, substituted or unsubstituted ester radical substituted or unsubstituted amine radical, substituted or unsubstituted amide radical, substituted or unsubstituted heteroaryl or substituted or unsubstituted aryl radical
  • n is between 1 and 1000,
  • m is between 0 and 1000 and
  • l is between 1 and 1000.

The compound l is designed, by selection of its substituent groups, to exhibit a colour change in range of + or -10° C, preferably + or - 5° C.

The synthesized polythiophene is mixed with a carrier system or liquid medium. Depending upon the specific polythiophene used, the carrier system can be aqueous or organic. The polythiophene can be used in the carrier system as a mechanical separation, colloidial solution, or a molecular solution. Also, surfactants, anionic, cationic or non-anionic, can be used if necessary in the carrier system to ensure uniform distribution of the polythiophene in the system.

For the example described in the Background, a polythiophene is synthesized to exhibit the calor change at about 3°C (38°F) and maintain that color change at lower temperatures when used in a carrier system, which system is placed in heat transfer relationship with the tray (article) the temperature of which is being monitored. Conversely, if the hot tray is to be maintained at about 82°C (180°F) or higher then a polythiophene is synthesized to change color at about 82°C (180°F). The polythiophene is mixed in a carrier system, which cancer system is placed in heat exchange relationship, such as by coating, at least a portion of the tray.

In a preferred embodiment, polythiophene in an amount of 0.05 to 5.0% by weight based on the total weight of the system, preferably 0.2 to 0.8% weight, is mixed with an organic solvent. Suitable solvents include tetrahydrofuran, chloroform, methylene chloride, toluene, and N-methylpyrrolidone.

In yet another embodiment, polythiophene in an amount of 1.0-25% by weight based on the total weight of the system, preferably 7.0 to 14% weight, is dispersed in commercially available printable ink formulations, e.g. oil with resins, pigment extenders and other additives. The system can be printed using conventional methods such as ink-jet and letter press. Examples of ink formulations that polythiophene can be dispersed in can include combinations of resins such as cellulose, nitrocellulose with co-binders including polyamides, polyester amides, alkyd, epoxy acrylates, amine acrylates, polyurethanes, and polyvinyl butyral (UNI-REZ, UNI-JET, BECKOSOL, EPOTUF), suitable oils such as napthenic petroleum oils and vegetable oils, e.g. soy beau oil, and suitable pigment extenders and additives that can include organic acids and esters of organic acids such as malic acid and organic solvents such as 1,5-pentanedial, diethylene glycol, along with other alcohols and related compounds (VERTEC, SYLFAT, UNI-KYD, and ICM, DY-SOLVE lines of additives.).

In yet another embodiment of an ink formulation system, polythiophene is dispersed in an ink formulation in an amount of about 1 .0 to 25% by weight of the total system, preferably 7.0 to 14% weight. The ink formulation system can then be printed on at least a portion of a suitable substrate, e.g. a portion of paper, plastic, or ceramic food/beverage containers, a portion of packaging materials for foods and goods, labels, a portion of labels, stickers, etc., using conventional printing methods. The polythiophenes dispersed in the system can be in particulate form and have diameters in the range of between about 0.01 - 0.1 microns thereby rendering the system suitable for fine printing.

In another embodiment of the invention, the system is applied to the article as a coating on an area of the article, or the entire article, which will be visible during the expected use of the article: The coating can be applied by any technique known in the art, such as by brush, roller, spraying, etc. Accordingly, the coatings typically have a thickness of 0.1 to 1000 microns. The carrier system can also be absorbed on a surface or both absorbed and adsorbed on a surface.

The method of the invention uses polythiophenes that visually and reversibly change color at a prescribed temperature in the range of -40 to 180 °C and are thermally stable to high temperatures in a range of about 200-300 °C- The temperature of the color change of the polythiophenes, hereinafter the thermochromic transition, and the high and low temperature colors can be tailored by chemical modification of the polythiophenes.

In synthesizing a polythiophene for a specific design temperature, eg. for the series of poly(3-alkylthiophene)s there is roughly an inverse correlation with the length of the n-alkane substituent and the temperature of the thermochromic transition for both the regiorandom (R1=alkyl, R4=alkyl, n=0-8, m=0.2, 1=40-80, R2, R3, R5, R6=H) and regioregular (R1=alkyl, n= 40-80, m=0, R2,R5,R6=H), poly(3-n-alkylthiophene)s. For regiorandom polymers longer substituents such as n-hexadecyl have lower temperature thermochromic, transitions (81 °C) than shorter chain substituents such as n-octyl (130 °C). The regioregular polymers have higher thermochromic transitions than the regioregular polymers but the same inverse correlation with chainlength is observed. The n-hexadecyl and n-octyl have thermochromic transition centered around 125 and 175 °C. As long as the number of thiophene units in the polymer is approximately greater than sixteen the thermochromic transitions is molecular weight independent. Oligothiophenes (n+m+1 < 16) have lower temperature thermochromic transitions than the polythiophenes (n+m+1 > 16).

Yet another aspect of the invention comprises paint, plastic or rubber composites comprised of the polythiophenes that are one color at temperatures below the thermochromic transition and are another color while above the transition. Both the low and high temperature colors and the temperature of the color change vary as a function of the substituent groups R1, R2, R3, R4, R5, and R6, the number of repeat units (1), and regioregularity of the repeat units (n and m).

The invention also comprises polythionphenes that can be used as pure compounds or can be incorporated into paints including polyurethanes, polysiloxanes, polyacrylates, and other related polymer-based paints and coatings with about 0-5 % polymer based pigment with retention of the thermochromic behavior. The thermochromic polymer-based pigments can be incorporated via injection molding or extrusion into many commercially important plastics such as poly(ethylene terephthalate) (PET), polysytrene, polyethylene (HDPE and LDPE), other polyolefins, polydienes, polycarbonates, polyacrylics, polyacrylic acids, polyacrylamides, polymethacrylics, polyvinyl ethers, polyvinyl halides, poly(vinyl nitrile)s poly vinyl esters, polyesters, polysofones, polysulfonamides, polyamides, polyimines, polyimides, carbohydrates, and polymer mixtures and copolymers. The plastics retain a visually retrievable thermochromic response with pigment loadings of about 0.5 % polymer-based pigment. The sensor system can be used as a safety feature or a thermal sensor for stoves, baking utensils or pans, radiator caps, cooling racks, paper/plastic coffee cups and lids, baby bottles, cooking utensils, cooking ware, fire safety, food packaging, instrument sterilization, novelty items, food preparation and handling equipment, warning labels, packaging film, microwave dishes, frozen food packages, beverage bottles, cable or wire coverings, motor and engine parts, breaking systems, automobile or truck tires, bathtub coatings, road signs, refrigerator cases, interior wall paint and other substrates and/or articles where a visual indication of a temperature change is important.

Brief Description of the Drawing(s)

  • Fig. 1 is a photograph depicting a polythiophene film of the invention on glass, hot and cold.
  • Fig. 2 is a graph depicting the visible spectrum of a polythiophene film of the invention as a function of temperature.
  • Fig. 3 is a graph depicting a plot of the wavelength of the absorption band edge at half the maximum intensity for a polythiophene as a function of temperature.

Description of the Preferred Embodiment(s)

Referring to Fig. 1, a photograph of two films is depicted, one at room temperature and one above the thermochromic transition. The films are comprised of a polythiophene wherein R1 and R4 are -(CH2)17CH3, R2, R3,R5 and R6 are H, n is 0.8, m is 0.2, and 1 is between 40 and 80. The film changes color at about 60 °C.

Referring to Fig. 2, a graph of the visible spectrum of a polythiophene wherein R1 = R4 = -(CH2)17CH3, R2 = R3 = R5 = R6 = H as a function of temperature is shown. The graph displays a dramatic difference in absorption around 500 nm. At low temperature the absorbance is quite high while at high temperature the absorbance is low. This feature in the optical spectrum is responsible for the visual color change of the polythiophene.

Referring to Fig. 3, a plot of the wavelength of the absorption band edge at half of the maximum intensity for a polythiophene as a function of temperature is shown. The inversion point for the color transition for the polythiophene wherein R1 = R4 = -(CH2)17CH3, R2 = R3 = R5 = R6 = H occurs at about 62°C while the inversion point for the color transition for the polythiophene wherein R1 = R4 = -(CH2)15CH3, R2 = R3 = R5 = R6 = H occurs at 81° C. This indicates that the temperature of the thermochromic transition can be changed by altering the substituents on the polymer backbone.

Based on the teachings of this disclosure, one skilled in the art could design a polythiophene with a predetermined thermochromic transition by investigating the systematic trends of the thermochromic transition as a function of polythiophene or oligothiophene structure. The temperature can be dropped by increasing the length of the alkyl substituent R1 or by via the preparation of oligmers. The temperature of the thermochromic transition can be increased by preparing regioregular poly(3-alkylthiophene)s or using shorter alkylsubstituents (R1).)

The invention will further be described with reference to following non-limiting

examples. Preparation of Poly(3-alkylthiophene)s 3-n-octadecylthiophene

3-n-octadecylthiophene was prepared as set forth in Kumda et al Bull. Chem Soc. Jpn. 1976, 49, 1958-1969 and Tetrahedron 1982, 38, 3347-3354 . A dry 1000 mL 2 neck flask was charged with Mg ribbon (3.34 g, 137 mmol) under N2 followed by addition of ~200 mL of anhydrous Et2O. The flask was cooled in an ice bath (0° C). In a separate 500 mL flask 40 g (120 mmol) of n-C18H37Br was dissolved in ~200 mL of anhydrous Et2O under N2. The Et2O solution of n-C18H37Br was slowly transfer into the flask containing the Mg ribbon, with sonication, stirring, and addition of I2 to initiate Grignard. After complete addition of n-C18H37Br to the Mg the reaction mixture was allowed to stir overnight to allow for complete formation of the Grignard reagent (n-C18H37MgBr). A dry 1000 mL 3-neck flask was charged with 0.540 g of 1,3-Bis(diphenylphosphino)propane nickel (II) chloride was added under nitrogen followed by ~100 mL of anhydrous Et2O and 11.25 mL (120 mmol) of 3-bromothiphene. The flask was then cooled in an ice bath (0° C). The Et2O solution of n-C18H37MgBr was slowly added to the flask containing the nickel catalyst and the 3-bromothiophene to prevent the generation of excessive heat and high concentrations of n-C18H37MgBr in the presence of the catalyst. The reaction mixture was allowed to stir overnight resulting in the formation of two layers. The top Et2O layer contained the product and the second small lower dark brown oily layer contained the Ni catalyst and the Mg salts. The primary side product of the reaction was the coupling product of two equivalents of n-C18H37MgBr to form C36H74, which was easily separated form the product since it had low solubility in Et2O. The product was purified via aqueous workup followed by filtration and removal of the Et2O by rotoevaporation to leave the impure low melting solid product. This solid was redissolved in a minimal amount of Et2O (~ 30 mL) followed by addition of ~250 mL of MeOH and placed into low temperature freezer (-80 °C) for recrystalization. The yield of this reaction is about 80-90 %.

Poly(3-n-ocatdecylthiophene)

Poly(3-n-ocatdecylthiophene) was prepared as forth in Leclerc et. al. Makromol. Chem. 1989, 190, 3105-3116 . 3-ocatadecylthiophene (10 g, 30 mmol) was added to a dry 500 mL round bottom flask under N2 and dissolved in 100 mL of CHCl3. In a separate dry 500 mL flask under N2 was added FeCl3 (24.3 g, 90 mmol) and 100 mL of CHCl3. The CHCl3 solution of 3-ocatadecylthiophene was slowly transferred to the flask containing the FeCl3 resulting in the generation of heat. The contents of the flask were stirred at RT for 24-36 h. The reaction mixture was then slowly dripped into rapidly stirring MeOH (1 L) resulting in the precipitation of the polymer. The precipitate was collected via vacuum filtration, washed with MeOH (100 mL) and redissolved in ~150 mL of CHCl3 with the assistance of sonication. The solution was washed/reduced with aqueous hydrazine (2x100 mL, 0.5 M) and aqueous HCl (2x100 mL, 0.5 M). The organic layer was slowly dripped into of rapidly stirring MeOH (1 L) to reprecipitate the polymer which was collected by vacuum filtration.

One skilled in the art would recognize that other known methods only precipitate the polymer once and reduce/purify the polymer via Sohxlet extraction with MeOH. Further, it will be apparent to one skilled in the art that the polymerization reaction can be carried out in methylene chloride as opposed to chloroform if it would be more economical or EPA acceptable.

Development of Thermochromic Paints

Scheme 1

50 mg of poly (3-octadecylthiophene) prepared via the procedure shown in Scheme 1, where R = C18C37 was dissolved in 2.0 ml of tetrahydrofuran. This deeply colored solution was added to 25 ml of Minwax fast drying polyurethane (clear semi-gloss). This provides a uniform mixture that was applied to paper, plastic, and painted metal surfaces. Upon drying (20 min) the surfaces where heated to 100°C for 1 min to remove any residual solvent from the coating and then allowed to cool to room temperature. After cooling to room temperature the "painted" surfaces are red. When the red surfaces are heated above 60-70°C the color of the surfaces changes from red to yellow. The color change is accompanied by a change in the visual transparency of the surface coating. When the red coating is opaque while when yellow the coating is translucent. This process is very similar to what is observed for the pure poly (3-octadecylthiophene). The coating adheres strongly to paper, plastic, and painted metal surfaces. Addition of blue pigments such as ultramarine blue allow adjustment of the cold and hot colors. The color can be adjusted to a gray/purple when cold and bright green when hot. The thermochromic paints can be applied in various manners including brush, sponge, roller, and airbrush.

Scheme 2

Non-regioregular 3-alkoxy-4-alkyl substituted polythiophenes for thermochromic applications have been synthesized according to Scheme 2, where R = CH3 and R'= C18H37. These polymers can be used as a reversible thermal sensor that detects excursion through a single temperature with visual or optical detection. At temperatures below the thermochromic transition polymer films are violet, above the transition the films are orange. The temperature of the thermochromic transition can be adjusted by variation of the backbone alkyl or alkoxy substituents.

All of the polythiophene-based pigments described herein, most particularly 3-alkylpolythiophenes and 3-alkoxy-4-alkylpolythiophenes, can be incorporated into polymer based-paints such as polyurethanes and polysiloxanes or plastics and retain the thermochromic behavior. Upon incorporation of the thermochromic polymer based pigments into plastics the materials have been determined to be viable for FDA approval.

Development of Thermochromic Plastics

Two hundred g of polypropylene was weighed into a small self-sealing bag. 1.0 g of poly(3-octadecylthiophene) was added to the polypropylene. The mixture was vigorously shaken until the poly(3-octadecylthiophene) was well dispersed in the polypropylene. The mixture was then added to the addition funnel of a BOY 22-D injection molding machine to produce polypropylene chips containing 0.5% by weight of poly(3-octadecylthiophene). When the red polypropylene chips are heated to temperatures above 60-70° C the chips turn yellow. When the chips are removed from the heat they return to the low temperature color as at a rate comparable to that of the cooling rate of the chips. The color change is accompanied by a change in transparency. The chips are significantly more transparent at high temperatures than at low temperatures.

Two hundred g of polystyrene was weighed into a small self-sealing bag. 1.0 g of poly(3-octadecylthiophene) was added to the polystyrene. The mixture was vigorously shaken until the poly(3-octadecylthiophene) was well dispersed in the polystyrene. The mixture was then added to the addition funnel of a BOY 22-D injection molding machine to produce polystyrene chips containing 0.5% by weight of poly(3-octadecylthiophene). When the red polystyrene chips are heated to temperatures above 60-70° C the chips turn yellow. When the chips are removed from the heat they return to the low temperature color' as at a rate significantly slower to that of the cooling rate of the chips. The color change is accompanied by a change in transparency. The chips are significantly more transparent at high temperatures than at low temperatures.

Development of Thermochromic Coatings

12.5 mg of poly(3-octadecylthiophene) was added to a 25mL solution of poly(vinylidine fluoride) (PVDF) in THF (50 g/L of PVDF). The mixture was sonicated for 3 h to form a homogeneous solution. The solutions were solution cast onto silicon wafers and dried at 50° C to form red films. When heated above 60-70° C the PVDF films containing 1.0 % poly(3-octadecylthiophene) changed from red to yellow. When the films were allowed to cool back to room temperature the films changed back to red.


Anspruch[de]
Verfahren zur Behandlung eines Gegenstands, um die Detektierung mittels eines Farbwechsels zu ermöglichen, wenn der Gegenstand eine spezifische Temperatur erreicht oder überschreitet, bei dem mindestens ein Teil des Gegenstands mit einer thermochromen Temperaturindikatorzusammensetzung behandelt wird, wobei sich die Zusammensetzung in Wärmetauschbeziehung mit dem Gegenstand befindet, dadurch gekennzeichnet, dass die Zusammensetzung eine Zusammensetzung auf Polymerbasis ist, die ein Trägermedium und 0,05 bis 5 Gew.%, bezogen auf die Gesamtzusammensetzung, von einer Verbindung mit der folgenden Struktur umfasst: wobei R1 bis R6 ein Wasserstoff, substituierter oder unsubstituierter Alkylrest, substituierter oder unsubstituierter Alkoxyrest, substituierter oder unsubstituierter Arylrest, substituierter oder unsubstituierter Thioalkylrest, substituierter oder unsubstituierter Trialkylsilylrest, substituierter oder unsubstituierter Acylrest, substituierter oder unsubstituierter Esterrest, substituierter oder unsubstituierter Aminrest, substituierter oder unsubstituierter Amidrest, substituierter oder unsubstituierter Heteroarylrest oder substituierter oder unsubstituierter Arylrest sind, n zwischen 1 und 1000 liegt, m zwischen 0 und 1000 liegt und 1 zwischen 1 und 1000 liegt, und dass die Struktur der Verbindung I durch Auswahl ihrer Substituentengruppen ein solches Design hat, dass sie einen Farbwechsel in einem Bereich von plus oder minus 10°C zeigt, wenn in dem Gegenstand die Designtemperatur oder eine Temperatur jenseits der Designtemperatur erreicht worden ist, wobei die Designtemperatur im Bereich von -40 bis 180°C liegt. Verfahren nach Anspruch 1, wobei die Zusammensetzung einen Farbwechsel in einem Bereich von plus oder minus 5°C zeigt. Verfahren nach Anspruch 1 oder 2, wobei die Designtemperatur jede gewählte Temperatur innerhalb des Bereichs ist. Verfahren nach einem der vorhergehenden Ansprüche, wobei das Trägermedium aus Polyurethanen; Elastomeren einschließlich Polysiloxanen und Polydienen; Polyacrylaten, Poly(ethylenterephthalat)en (PET), Polystyrolen, Polyolefinen einschließlich Polyethylenen (HDPE und LDPE) und Polypropylen, Polycarbonaten, Polyacrylen, Polyacrylsäuren, Polyacrylamiden, Polymethacrylen, Polyvinylethern, Polyvinylhalogeniden, Poly(vinylnitril)en, Polyvinylestern, Polyestern, Polysulfonen, Polysulfonamiden, Polyamiden, Polyiminen, Polyimiden, Kohlehydraten und organischen Lösungsmitteln einschließlich Tetrahydrofuran, Chloroform, Methylenchlorid, Toluol und N-Methylpyrrolidon ausgewählt ist. Verfahren nach einem der vorhergehenden Ansprüche, bei dem in Formel I R1 und R4 Alkylgruppen sind, R2 und R3 Alkoxygruppen oder Wasserstoff sind, und R5 und R6 Wasserstoff sind. Verfahren nach Anspruch 5, wobei R1 und R4 jeweils Alkyl sind, R2, R3, R5 und R6 H sind, n 0,8 ist, m 0,2 ist und 1 zwischen 40 und 80 liegt. Verfahren nach Anspruch 6, wobei R1 und R4 jeweils - (CH2)17CH3 sind, wobei die Zusammensetzung ferner dadurch gekennzeichnet ist, dass eine Niedrigtemperaturfarbe rot ist, eine Hochtemperaturfarbe gelb ist, und der Farbwechsel der Zusammensetzung bei etwa 60°C erfolgt. Verfahren nach einem der vorhergehenden Ansprüche, wobei das Medium eine Tintenrezeptur ist. Verfahren nach einem der vorhergehenden Ansprüche, wobei die Behandlung Bürsten umfasst. Verfahren nach einem der Ansprüche 1 bis 8, wobei die Behandlung Walzen umfasst. Verfahren nach einem der Ansprüche 1 bis 8, wobei die Behandlung Sprühen umfasst. Verfahren nach einem der Ansprüche 1 bis 8, wobei die Behandelung das Mischen der Zusammensetzung mit mindestens einem Teil des Gegenstands umfasst. Verfahren nach einem der Ansprüche 1 bis 8 oder Anspruch 12, wobei die Behandelung das Beschichten mindestens eines Teils des Gegenstands umfasst. Verfahren nach einem der Ansprüche 1 bis 8, Anspruch 12 oder Anspruch 13, wobei die Behandelung das Drucken der Zusammensetzung auf mindestens einen Teil des Gegenstands umfasst. Thermochrome Temperaturindikatorzusammensetzung auf Polymerbasis, die einen Farbwechsel im Bereich von plus oder minus 10°C zeigt, wenn sie eine spezifische Temperatur in einem Bereich von -40 bis 180°C erreicht oder überschreitet, wobei die Zusammensetzung eine Verbindung mit der folgenden Struktur umfasst: wobei R1 und R4 jeweils Alkylgruppen sind, R2, R3, R5, und R6 jeweils Wasserstoff sind, 1 = 40-80 ist und entweder n~0,8 und m~0,2 oder n = 40-80 und m = 0 ist, und ein Trägermedium, wobei die Verbindung in dem Medium in einer Menge von 0,05 bis 5 Gew.% vorhanden ist, bezogen auf das Gesamtgewicht der Zusammensetzung. Zusammensetzung nach Anspruch 15, wobei R1 und R4 n-Hexadecyl oder n-Octadecyl sind. Zusammensetzung nach Anspruch 15, wobei R1 und R4 n-Octyl sind. Zusammensetzung nach einem der Ansprüche 15 bis 17, wobei die Verbindung in dem Medium in einer Menge von 1,0 bis 5 Gew.% vorhanden ist, bezogen auf das Gesamtgewicht der Zusammensetzung. Zusammensetzung nach einem der Ansprüche 15 bis 18, wobei die Verbindung in der Zusammensetzung in einer Menge von etwa 0,5 Gew.% vorhanden ist, bezogen auf das Gesamtgewicht der Zusammensetzung. Zusammensetzung nach einem der Ansprüche 15 bis 19, wobei das Medium eine Tintenrezeptur ist. Zusammensetzung nach Anspruch 20, wobei die Tintenrezeptur Öle, Harze, Pigmentstreckungsmittel und Additive umfasst. Gegenstand, der mindestens auf einem Teil von dessen Oberfläche eine Zusammensetzung nach einem der Ansprüche 15 bis 21 bedruckt ist. Gegenstand, der auf mindestens einem Teil von dessen Oberfläche mit einer Zusammensetzung nach einem der Ansprüche 15 bis 21 beschichtet ist. Gegenstand, der zumindest teilweise mit einer Zusammensetzung nach einem der Ansprüche 15 bis 21 gemischt ist. Verfahren zum Erfassen, wann ein Gegenstand eine spezifische Temperatur erreicht oder überschreitet, welches: die Behandelung mindestens eines Teils des Gegenstands mit einer Zusammensetzung nach einem der Ansprüche 15 bis 21, und das Erfassen, wann der Gegenstand die spezifische Temperatur erreicht oder überschritten hat, umfasst.
Anspruch[en]
A method of treating an article to enable detection by means of a colour change when the article meets or exceeds a specific temperature, which method comprises treating at least a portion of the article with a thermochromic temperature indicator composition, the composition being in heat exchange relationship with the article, characterised in that said composition is a polymer-based composition comprising a carrier medium and 0.05 to 5% by weight, based on the total composition, of a compound having the following structure: wherein R1-R6 = a hydrogen, substituted or unsubstituted alkyl radical, substituted or unsubstituted alkoxy radical, substituted or unsubstituted aryl radical, substituted or unsubstituted thioalkyl radical, substituted or unsubstituted trialkylsilyl radical, substituted or unsubstituted acyl radical, substituted or unsubstituted ester radical, substituted or unsubstituted amine radical, substituted or unsubstituted amide radical, substituted or unsubstituted heteroaryl radical or substituted or unsubstituted aryl radical, n is between 1 and 1000, m is between 0 and 1000, and 𝓁 is between 1 and 1000; and in that the structure of the compound I is designed, by selection of its substituent groups, to exhibit a colour change in a range of plus or minus 10°C when said design temperature or a temperature beyond the design temperature is reached in the article, said design temperature being in the range from -40 to 180°C. The method of claim 1 wherein the composition will exhibit a colour change in a range of plus or minus 5°C. The method of claim 1 or claim 2 wherein the design temperature is any selected temperature within the range. The method of any preceding claim wherein the carrier medium is selected from polyurethanes; elastomers including polysiloxanes and polydienes; polyacrylates, poly(ethylene terephthalate)s (PET), polystyrenes, polyolefins including polyethylenes (HDPE and LDPE) and polypropylene, polycarbonates, polyacrylics, polyacrylic acids, polyacrylamides, polymethacrylics, polyvinyl ethers, polyvinyl halides, poly (vinyl nitrile)s, polyvinyl esters, polyesters, polysulfones, polysulfonamides, polyamides, polyimines, polyimides, carbohydrates, and organic solvents including tetrahydrofuran, chloroform, methylene chloride, toluene, and N-methylpyrrolidone. The method of any preceding claim wherein in formula I R1 and R4 are alkyl groups, R2 and R3 are alkoxy groups or hydrogen and R5 and R6 are hydrogen. The method of claim 5 wherein R1 and R4 are both alkyl, R2, R3, R5, and R6 are H, n is 0.8, m is 0.2, and 𝓁 is between 40 and 80. The method of claim 6 wherein R1 and R4 are both - (CH2)17CH3, the composition being further characterised in that a low temperature colour is red, a high temperature colour is yellow, and the colour change of the composition occurs at about 60°C. The method of any preceding claim wherein said medium is an ink formulation. The method of any fee claim wherein treating comprises brushing. The method of any one of claims 1 to 8 wherein treating comprises rolling. The method of any one of claims 1 to 8 wherein treating comprises spraying. The method of any one of claims 1 to 8 wherein treating comprises: admixing the composition with at least a portion of the article. The method of any one of claims 1 to 8 or claim 12 wherein treating comprises coating at least a portion of the article. The method of any one of claims 1 to 8, claim 12 or claim 13 wherein treating comprises printing the composition on at least a portion of the article. A thermochomic polymer-based temperature indicator composition which exhibits a colour change in a range of plus or minus 10°C when it reaches or exceeds a specific temperature in a range from -40 to 180°c, which composition comprises: a compound having the following structure: wherein R2 and R4 are both alkyl groups, R2, R3, R5, and R6 are all hydrogen, 𝓁 = 40-80 and either n≈0.8 and m≈0.2 or n = 40-80 and m = 0 and a carrier medium, said compound being present in the medium in an amount of 0.05 to 5% by weight based on the total weight of the composition. The composition of claim 15 wherein R1 and R4 are n-hexadecyl or n-octadecyl. The composition of claim 15 wherein R1 and R4 are n-octyl. The composition of any one of claims 15 to 17 wherein said compound is present in the medium in an amount of 1.0 to 5% by weight based on the total weight of the composition. The composition of any one of claims 15 to 18 wherein said compound is present in the composition in an amount of about 0.5% by weight based on the total weight of the composition. The composition of any one of claims 15 to 19 wherein the medium is an ink formulation. The composition of claim 20 wherein the ink formulation comprises oils, resins, pigment extenders and additives. An article having printed on at least a portion of a surface thereof a composition according to any one of claims 15 to 21. An article having coated on at least a portion of a surface thereof a composition according to any one of claims 15 to 21. An article of at least a portion of which is admixed with a composition according to any one of claims 15 to 21. A method of detecting when an article meets or exceeds a specific temperature which comprises: treating at least a portion of the article with a composition according to any one of claims 15 to 21, and detecting when the article has met or exceeded the specific temperature.
Anspruch[fr]
Procédé de traitement d'un objet pour permettre la détection, au moyen d'un changement de couleur, du moment où l'objet atteint ou dépasse une température spécifique, lequel procédé comprend le traitement d'au moins une partie de l'objet avec une composition d'indicateur de température thermochromique, la composition étant en relation d'échange de chaleur avec l'objet, caractérisé en ce que ladite composition est une composition à base de polymère, comprenant un milieu support et 0,05 à 5 % en poids, par rapport à la composition totale, d'un composé ayant la structure suivante : dans laquelle R1-R6 = hydrogène, radical alkyle substitué ou non substitué, radical alcoxy substitué ou non substitué, radical aryle substitué ou non substitué, radical thioalkyle substitué ou non substitué, radical trialkylsilyle substitué ou non substitué, radical acyle substitué ou non substitué, radical ester substitué ou non substitué, radical amine substitué ou non substitué, radical amide substitué ou non substitué, radical hétéroaryle substitué ou non substitué ou radical aryle substitué ou non substitué, n est compris entre 1 et 1000, m est compris entre 0 et 1000, et 1 est compris entre 1 et 1000 ; et en ce que la structure du composé I est conçue, par sélection de ses groupes substituants, de façon à présenter un changement de couleur dans une plage de plus ou moins 10°C quand ladite température donnée ou une température supérieure à celle-ci est atteinte par l'objet, ladite température donnée étant située dans la plage allant de -40 à 180°C. Procédé selon la revendication 1, dans lequel la composition va présenter un changement de couleur dans une plage de plus ou moins 5°C. Procédé selon la revendication 1 ou la revendication 2, dans lequel la température donnée est une température sélectionnée quelconque à l'intérieur de la plage. Procédé selon l'une quelconque des revendications précédentes, dans lequel le milieu support est choisi parmi les polyuréthanes ; les élastomères comprenant les polysiloxanes et les polydiènes ; les polyacrylates, les polyéthylène téréphtalates (PET), les polystyrènes, les polyoléfines comprenant les polyéthylènes (HDPE et LDPE) et le polypropylène, les polycarbonates, les polyacryliques, les poly(acide acrylique), les polyacrylamides, les polyméthacryliques, les polyvinyléthers, les poly(halogénure de vinyle), les polyvinylnitriles, les poly(ester de vinyle), les polyesters, les polysulfones, les polysulfonamides, les polyamides, les polyimines, les polyimides, les hydrates de carbone, et les solvants organiques comprenant le tétrahydrofurane, le chloroforme, le chlorure de méthylène, le toluène, et la N-méthylpyrrolidone. Procédé selon l'une quelconque des revendications précédentes, dans lequel, dans la formule I, R1 et R4 sont des groupes alkyle, R2 et R3 sont des groupes alcoxy ou hydrogène et R5 et R6 sont hydrogène. Procédé selon la revendication 5, dans lequel R1 et R4 sont tous deux alkyle, R2, R3, R5 et R6 sont H, n vaut 0,8, m vaut 0,2, et 1 est compris entre 40 et 80. Procédé selon la revendication 6, dans lequel R1 et R4 sont tous deux -(CH2)17CH3, la composition étant en outre caractérisée en ce que la couleur à basse température est rouge, la couleur à température élevée est jaune, et le changement de couleur de la composition se produit à environ 60°C. Procédé selon l'une quelconque des revendications précédentes, dans lequel ledit milieu est une formulation d'encre. Procédé selon l'une quelconque des revendications précédentes, dans lequel le traitement comprend une application à la brosse. Procédé selon l'une quelconque des revendications 1 à 8, dans lequel le traitement comprend une application au rouleau. Procédé selon l'une quelconque des revendications 1 à 8, dans lequel le traitement comprend une pulvérisation. Procédé selon l'une quelconque des revendications 1 à 8, dans lequel le traitement comprend : le mélange de la composition avec au moins une partie de l'objet. Procédé selon l'une quelconque des revendications 1 à 8 ou selon la revendication 12, dans lequel le traitement comprend l'application en revêtement sur au moins une partie de l'objet. Procédé selon l'une quelconque des revendications 1 à 8, selon la revendication 12 ou selon la revendication 13, dans lequel le traitement comprend l'application par impression de la composition sur au moins une partie de l'objet. Composition d'indicateur de température à base de polymère thermochromique, qui présente un changement de couleur dans une plage de plus ou moins 10°C quand elle atteint ou dépasse une température spécifique dans la plage allant de -40 à 180°C, laquelle composition comprend : un composé ayant la structure suivante : dans laquelle R2 et R4 sont tous deux des groupes alkyle, R2, R3, R5 et R6 sont tous hydrogène, 1 = 40-80 et soit n ≈ 0,8 et m = 0,2, soit n = 40-80 et m = 0 et un milieu support, ledit composé étant présent dans le milieu en une quantité de 0,05 à 5 % en poids par rapport au poids total de la composition. Composition selon la revendication 15, dans laquelle R1 et R4 sont n-hexadécyle ou n-octadécyle. Composition selon la revendication 15, dans laquelle R1 et R4 sont n-octyle. Composition selon l'une quelconque des revendications 15 à 17, dans laquelle ledit composé est présent dans le milieu en une quantité de 1,0 à 5 % en poids par rapport au poids total de la composition. Composition selon l'une quelconque des revendications 15 à 18, dans laquelle ledit composé est présent dans la composition en une quantité d'environ 0,5 % en poids par rapport au poids total de la composition. Composition selon l'une quelconque des revendications 15 à 19, dans laquelle le milieu est une formulation d'encre. Composition selon la revendication 20, dans laquelle la formulation d'encre comprend des huiles, des résines, des pigments de charge et des additifs. Objet sur au moins une partie ou surface duquel est appliquée par impression une composition selon l'une quelconque des revendications 15 à 21. Objet sur au moins une partie ou surface duquel est appliquée en revêtement une composition selon l'une quelconque des revendications 15 à 21. Objet dont au moins une partie est mélangée avec une composition selon l'une quelconque des revendications 15 à 21. Procédé pour détecter le moment où un objet atteint ou dépasse une température spécifique, qui comprend : le traitement d'au moins une partie de l'objet avec une composition selon l'une quelconque des revendications 15 à 21, et la détection du moment où l'objet a atteint ou dépassé la température spécifique.






IPC
A Täglicher Lebensbedarf
B Arbeitsverfahren; Transportieren
C Chemie; Hüttenwesen
D Textilien; Papier
E Bauwesen; Erdbohren; Bergbau
F Maschinenbau; Beleuchtung; Heizung; Waffen; Sprengen
G Physik
H Elektrotechnik

Anmelder
Datum

Patentrecherche

Patent Zeichnungen (PDF)

Copyright © 2008 Patent-De Alle Rechte vorbehalten. eMail: info@patent-de.com